Custom fabrication of reinforced lithium disilicate ceramic ingot.

Chander GN, Sasikala C, Mutukumar B, Dhanasekar N - Indian J Dent (2016 Jan-Mar)

Bottom Line: The sectioned ingot is ball milled along with 10% of nano zirconia by weight to obtain the desired powder.The compacted ceramic were sintered at 900°C to obtain ceramic ingots.The reinforced ceramic ingots were used in pressable ceramic machines to obtain the desired advantages of zirconia reinforcement and pressable ceramic system.

View Article: PubMed Central - PubMed

Affiliation: Department of Prosthodontics, SRM Dental College, Ramapuram, Chennai, Tamil Nadu, India.

ABSTRACT
A method of formulating a reinforcement lithium disilicate ceramic ingot was proposed. The ceramic ingot was broken manually with a mallet to finer particles. The sectioned ingot is ball milled along with 10% of nano zirconia by weight to obtain the desired powder. The reinforced powder is condensed in a 5 ml disposable syringe by powder slurry technique. The compacted ceramic were sintered at 900°C to obtain ceramic ingots. The reinforced ceramic ingots were used in pressable ceramic machines to obtain the desired advantages of zirconia reinforcement and pressable ceramic system.

No MeSH data available.


Related in: MedlinePlus

Sintered ceramic ingot
© Copyright Policy - open-access
Related In: Results  -  Collection

License
getmorefigures.php?uid=PMC4836100&req=5

Figure 3: Sintered ceramic ingot

Mentions: The packed material is removed and sintered in a ceramic furnace at 900°C to form an ingot [Figure 3]


Custom fabrication of reinforced lithium disilicate ceramic ingot.

Chander GN, Sasikala C, Mutukumar B, Dhanasekar N - Indian J Dent (2016 Jan-Mar)

Sintered ceramic ingot
© Copyright Policy - open-access
Related In: Results  -  Collection

License
Show All Figures
getmorefigures.php?uid=PMC4836100&req=5

Figure 3: Sintered ceramic ingot
Mentions: The packed material is removed and sintered in a ceramic furnace at 900°C to form an ingot [Figure 3]

Bottom Line: The sectioned ingot is ball milled along with 10% of nano zirconia by weight to obtain the desired powder.The compacted ceramic were sintered at 900°C to obtain ceramic ingots.The reinforced ceramic ingots were used in pressable ceramic machines to obtain the desired advantages of zirconia reinforcement and pressable ceramic system.

View Article: PubMed Central - PubMed

Affiliation: Department of Prosthodontics, SRM Dental College, Ramapuram, Chennai, Tamil Nadu, India.

ABSTRACT
A method of formulating a reinforcement lithium disilicate ceramic ingot was proposed. The ceramic ingot was broken manually with a mallet to finer particles. The sectioned ingot is ball milled along with 10% of nano zirconia by weight to obtain the desired powder. The reinforced powder is condensed in a 5 ml disposable syringe by powder slurry technique. The compacted ceramic were sintered at 900°C to obtain ceramic ingots. The reinforced ceramic ingots were used in pressable ceramic machines to obtain the desired advantages of zirconia reinforcement and pressable ceramic system.

No MeSH data available.


Related in: MedlinePlus