Limits...
Rapid prototyping for in vitro knee rig investigations of prosthetized knee biomechanics: comparison with cobalt-chromium alloy implant material.

Schröder C, Steinbrück A, Müller T, Woiczinski M, Chevalier Y, Weber P, Müller PE, Jansson V - Biomed Res Int (2015)

Bottom Line: Friction coefficients between these materials and polytetrafluoroethylene (PTFE) were additionally tested as this latter material is commonly used to protect pressure sensors in experiments.No statistical differences were found between friction coefficients of both materials to PTFE.UHMWPE shows higher friction coefficient at low axial loads for RPM, a difference that disappears at higher load.

View Article: PubMed Central - PubMed

Affiliation: Department of Orthopaedic Surgery, Physical Medicine and Rehabilitation, University Hospital of Munich (LMU), Campus Grosshadern, Marchioninistraße 15, 81377 Munich, Germany.

ABSTRACT
Retropatellar complications after total knee arthroplasty (TKA) such as anterior knee pain and subluxations might be related to altered patellofemoral biomechanics, in particular to trochlear design and femorotibial joint positioning. A method was developed to test femorotibial and patellofemoral joint modifications separately with 3D-rapid prototyped components for in vitro tests, but material differences may further influence results. This pilot study aims at validating the use of prostheses made of photopolymerized rapid prototype material (RPM) by measuring the sliding friction with a ring-on-disc setup as well as knee kinematics and retropatellar pressure on a knee rig. Cobalt-chromium alloy (standard prosthesis material, SPM) prostheses served as validation standard. Friction coefficients between these materials and polytetrafluoroethylene (PTFE) were additionally tested as this latter material is commonly used to protect pressure sensors in experiments. No statistical differences were found between friction coefficients of both materials to PTFE. UHMWPE shows higher friction coefficient at low axial loads for RPM, a difference that disappears at higher load. No measurable statistical differences were found in knee kinematics and retropatellar pressure distribution. This suggests that using polymer prototypes may be a valid alternative to original components for in vitro TKA studies and future investigations on knee biomechanics.

Show MeSH

Related in: MedlinePlus

Dependence of the coefficient of sliding friction with rising axial load for the tested parameters; whiskers define the 95% confidence interval.
© Copyright Policy
Related In: Results  -  Collection

License
getmorefigures.php?uid=PMC4388012&req=5

fig4: Dependence of the coefficient of sliding friction with rising axial load for the tested parameters; whiskers define the 95% confidence interval.

Mentions: With increasing load, a decrease of the friction coefficient was measured in the four groups (P < 0.001). The friction test with the bearing partner UHMWPE provided significant higher friction coefficients than with PTFE (P < 0.001; Figure 4). There was no interaction between load and material combination measurable (P = 0.52).


Rapid prototyping for in vitro knee rig investigations of prosthetized knee biomechanics: comparison with cobalt-chromium alloy implant material.

Schröder C, Steinbrück A, Müller T, Woiczinski M, Chevalier Y, Weber P, Müller PE, Jansson V - Biomed Res Int (2015)

Dependence of the coefficient of sliding friction with rising axial load for the tested parameters; whiskers define the 95% confidence interval.
© Copyright Policy
Related In: Results  -  Collection

License
Show All Figures
getmorefigures.php?uid=PMC4388012&req=5

fig4: Dependence of the coefficient of sliding friction with rising axial load for the tested parameters; whiskers define the 95% confidence interval.
Mentions: With increasing load, a decrease of the friction coefficient was measured in the four groups (P < 0.001). The friction test with the bearing partner UHMWPE provided significant higher friction coefficients than with PTFE (P < 0.001; Figure 4). There was no interaction between load and material combination measurable (P = 0.52).

Bottom Line: Friction coefficients between these materials and polytetrafluoroethylene (PTFE) were additionally tested as this latter material is commonly used to protect pressure sensors in experiments.No statistical differences were found between friction coefficients of both materials to PTFE.UHMWPE shows higher friction coefficient at low axial loads for RPM, a difference that disappears at higher load.

View Article: PubMed Central - PubMed

Affiliation: Department of Orthopaedic Surgery, Physical Medicine and Rehabilitation, University Hospital of Munich (LMU), Campus Grosshadern, Marchioninistraße 15, 81377 Munich, Germany.

ABSTRACT
Retropatellar complications after total knee arthroplasty (TKA) such as anterior knee pain and subluxations might be related to altered patellofemoral biomechanics, in particular to trochlear design and femorotibial joint positioning. A method was developed to test femorotibial and patellofemoral joint modifications separately with 3D-rapid prototyped components for in vitro tests, but material differences may further influence results. This pilot study aims at validating the use of prostheses made of photopolymerized rapid prototype material (RPM) by measuring the sliding friction with a ring-on-disc setup as well as knee kinematics and retropatellar pressure on a knee rig. Cobalt-chromium alloy (standard prosthesis material, SPM) prostheses served as validation standard. Friction coefficients between these materials and polytetrafluoroethylene (PTFE) were additionally tested as this latter material is commonly used to protect pressure sensors in experiments. No statistical differences were found between friction coefficients of both materials to PTFE. UHMWPE shows higher friction coefficient at low axial loads for RPM, a difference that disappears at higher load. No measurable statistical differences were found in knee kinematics and retropatellar pressure distribution. This suggests that using polymer prototypes may be a valid alternative to original components for in vitro TKA studies and future investigations on knee biomechanics.

Show MeSH