Preparation and preliminary dialysis performance research of polyvinylidene fluoride hollow fiber membranes.

Zhang Q, Lu X, Liu J, Zhao L - Membranes (Basel) (2015)

Bottom Line: The results showed that the clearance rate of urea and Lysozyme (LZM) were improved with increasing membrane area and fluid flow rate while the rejection of albumin from bovine serum (BSA) had little influence.The PVDF dialyzer with membrane area 0.69 m2 has the highest clearance rate to LZM and urea.The clearance rate of LZM was 66.8% and urea was 87.7%.

View Article: PubMed Central - PubMed

Affiliation: Institute of Biological and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387, China. haiyang19802005@163.com.

ABSTRACT
In this study, the separation properties of Polyvinylidene fluoride (PVDF) hollow fiber hemodialysis membranes were improved by optimizing membrane morphology and structure. The results showed that the PVDF membrane had better mechanical and separation properties than Fresenius Polysulfone High-Flux (F60S) membrane. The PVDF membrane tensile stress at break, tensile elongation and bursting pressure were 11.3 MPa, 395% and 0.625 MPa, respectively. Ultrafiltration (UF) flux of pure water reached 108.2 L∙h-1∙m-2 and rejection of Albumin from bovine serum was 82.3%. The PVDF dialyzers were prepared by centrifugal casting. The influences of membrane area and simulate fluid flow rate on dialysis performance were investigated. The results showed that the clearance rate of urea and Lysozyme (LZM) were improved with increasing membrane area and fluid flow rate while the rejection of albumin from bovine serum (BSA) had little influence. The high-flux PVDF dialyzer UF coefficient reached 62.6 mL/h/mmHg. The PVDF dialyzer with membrane area 0.69 m2 has the highest clearance rate to LZM and urea. The clearance rate of LZM was 66.8% and urea was 87.7%.

No MeSH data available.


Related in: MedlinePlus

The stress-strain curves of different PVDF membranes; the labels M-14.8, M-16.8, M-3, and M-20.8 are membranes with PEG content: 14.8, 16.8, 18.8 and 20.8 wt %, respectively.
© Copyright Policy
Related In: Results  -  Collection

License
getmorefigures.php?uid=PMC4384094&req=5

membranes-05-00120-f007: The stress-strain curves of different PVDF membranes; the labels M-14.8, M-16.8, M-3, and M-20.8 are membranes with PEG content: 14.8, 16.8, 18.8 and 20.8 wt %, respectively.

Mentions: As shown in Table 3 and Figure 7, the tensile stress increases from 7.4 MPa to 11.3 MPa and the porosity decreases from 88.8% to 85.1% at first, and then the tensile stress decreases from 11.3 MPa to 8.1 MPa and the porosity increases from 85.1% to 87.5%. The results also indicate that the bursting pressure increases with membrane porosity decreasing. Therefore, both the casting solution composition and membrane porosity can affect the tensile stress at break. The M-3 membrane has better mechanical properties than the other PVDF hollow fiber membranes.


Preparation and preliminary dialysis performance research of polyvinylidene fluoride hollow fiber membranes.

Zhang Q, Lu X, Liu J, Zhao L - Membranes (Basel) (2015)

The stress-strain curves of different PVDF membranes; the labels M-14.8, M-16.8, M-3, and M-20.8 are membranes with PEG content: 14.8, 16.8, 18.8 and 20.8 wt %, respectively.
© Copyright Policy
Related In: Results  -  Collection

License
Show All Figures
getmorefigures.php?uid=PMC4384094&req=5

membranes-05-00120-f007: The stress-strain curves of different PVDF membranes; the labels M-14.8, M-16.8, M-3, and M-20.8 are membranes with PEG content: 14.8, 16.8, 18.8 and 20.8 wt %, respectively.
Mentions: As shown in Table 3 and Figure 7, the tensile stress increases from 7.4 MPa to 11.3 MPa and the porosity decreases from 88.8% to 85.1% at first, and then the tensile stress decreases from 11.3 MPa to 8.1 MPa and the porosity increases from 85.1% to 87.5%. The results also indicate that the bursting pressure increases with membrane porosity decreasing. Therefore, both the casting solution composition and membrane porosity can affect the tensile stress at break. The M-3 membrane has better mechanical properties than the other PVDF hollow fiber membranes.

Bottom Line: The results showed that the clearance rate of urea and Lysozyme (LZM) were improved with increasing membrane area and fluid flow rate while the rejection of albumin from bovine serum (BSA) had little influence.The PVDF dialyzer with membrane area 0.69 m2 has the highest clearance rate to LZM and urea.The clearance rate of LZM was 66.8% and urea was 87.7%.

View Article: PubMed Central - PubMed

Affiliation: Institute of Biological and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387, China. haiyang19802005@163.com.

ABSTRACT
In this study, the separation properties of Polyvinylidene fluoride (PVDF) hollow fiber hemodialysis membranes were improved by optimizing membrane morphology and structure. The results showed that the PVDF membrane had better mechanical and separation properties than Fresenius Polysulfone High-Flux (F60S) membrane. The PVDF membrane tensile stress at break, tensile elongation and bursting pressure were 11.3 MPa, 395% and 0.625 MPa, respectively. Ultrafiltration (UF) flux of pure water reached 108.2 L∙h-1∙m-2 and rejection of Albumin from bovine serum was 82.3%. The PVDF dialyzers were prepared by centrifugal casting. The influences of membrane area and simulate fluid flow rate on dialysis performance were investigated. The results showed that the clearance rate of urea and Lysozyme (LZM) were improved with increasing membrane area and fluid flow rate while the rejection of albumin from bovine serum (BSA) had little influence. The high-flux PVDF dialyzer UF coefficient reached 62.6 mL/h/mmHg. The PVDF dialyzer with membrane area 0.69 m2 has the highest clearance rate to LZM and urea. The clearance rate of LZM was 66.8% and urea was 87.7%.

No MeSH data available.


Related in: MedlinePlus