Crystallographic plane-orientation dependent atomic force microscopy-based local oxidation of silicon carbide.

Ahn JJ, Jo YD, Kim SC, Lee JH, Koo SM - Nanoscale Res Lett (2011)

Bottom Line: It has been found that the AFM-based local oxidation (AFM-LO) rate on SiC is closely correlated to the atomic planar density values of different crystalline planes (a-plane, 7.45 cm-2; c-plane, 12.17 cm-2; and m-plane, 6.44 cm-2).Specifically, at room temperature and under about 40% humidity with a scan speed of 0.5 μm/s, the height of oxides on a- and m-planes 4H-SiC is 6.5 and 13 nm, respectively, whereas the height of oxides on the c-plane increased up to 30 nm.In addition, the results of AFM-LO with thermally grown oxides on the different plane orientations in SiC are compared.

View Article: PubMed Central - HTML - PubMed

Affiliation: School of Electronics and Information, Kwangwoon University, Seoul 139-701, Korea. smkoo@kw.ac.kr.

ABSTRACT
The effect of crystalline plane orientations of Silicon carbide (SiC) (a-, m-, and c-planes) on the local oxidation on 4H-SiC using atomic force microscopy (AFM) was investigated. It has been found that the AFM-based local oxidation (AFM-LO) rate on SiC is closely correlated to the atomic planar density values of different crystalline planes (a-plane, 7.45 cm-2; c-plane, 12.17 cm-2; and m-plane, 6.44 cm-2). Specifically, at room temperature and under about 40% humidity with a scan speed of 0.5 μm/s, the height of oxides on a- and m-planes 4H-SiC is 6.5 and 13 nm, respectively, whereas the height of oxides on the c-plane increased up to 30 nm. In addition, the results of AFM-LO with thermally grown oxides on the different plane orientations in SiC are compared.

No MeSH data available.


Oxide height as a function of scan speed on different 4H-SiC by AFM-LO.
© Copyright Policy - open-access
Related In: Results  -  Collection

License
getmorefigures.php?uid=PMC3211294&req=5

Figure 7: Oxide height as a function of scan speed on different 4H-SiC by AFM-LO.

Mentions: These results are shown in Figure 7, where the oxide heights versus the scan speed on a-, c-, and m-planes of 4H-SiC are compared. The oxide height decreases as the scan speed increases on all a-, c-, and m-planes of 4H-SiC, suggesting that a longer anodization time resulted in an increased oxidation rate. It has clearly been shown that the AFM-LO rate on c-plane 4H-SiC is significantly higher than the other plane orientations, which may be related to the areal density of the first layer for the different surfaces.


Crystallographic plane-orientation dependent atomic force microscopy-based local oxidation of silicon carbide.

Ahn JJ, Jo YD, Kim SC, Lee JH, Koo SM - Nanoscale Res Lett (2011)

Oxide height as a function of scan speed on different 4H-SiC by AFM-LO.
© Copyright Policy - open-access
Related In: Results  -  Collection

License
Show All Figures
getmorefigures.php?uid=PMC3211294&req=5

Figure 7: Oxide height as a function of scan speed on different 4H-SiC by AFM-LO.
Mentions: These results are shown in Figure 7, where the oxide heights versus the scan speed on a-, c-, and m-planes of 4H-SiC are compared. The oxide height decreases as the scan speed increases on all a-, c-, and m-planes of 4H-SiC, suggesting that a longer anodization time resulted in an increased oxidation rate. It has clearly been shown that the AFM-LO rate on c-plane 4H-SiC is significantly higher than the other plane orientations, which may be related to the areal density of the first layer for the different surfaces.

Bottom Line: It has been found that the AFM-based local oxidation (AFM-LO) rate on SiC is closely correlated to the atomic planar density values of different crystalline planes (a-plane, 7.45 cm-2; c-plane, 12.17 cm-2; and m-plane, 6.44 cm-2).Specifically, at room temperature and under about 40% humidity with a scan speed of 0.5 μm/s, the height of oxides on a- and m-planes 4H-SiC is 6.5 and 13 nm, respectively, whereas the height of oxides on the c-plane increased up to 30 nm.In addition, the results of AFM-LO with thermally grown oxides on the different plane orientations in SiC are compared.

View Article: PubMed Central - HTML - PubMed

Affiliation: School of Electronics and Information, Kwangwoon University, Seoul 139-701, Korea. smkoo@kw.ac.kr.

ABSTRACT
The effect of crystalline plane orientations of Silicon carbide (SiC) (a-, m-, and c-planes) on the local oxidation on 4H-SiC using atomic force microscopy (AFM) was investigated. It has been found that the AFM-based local oxidation (AFM-LO) rate on SiC is closely correlated to the atomic planar density values of different crystalline planes (a-plane, 7.45 cm-2; c-plane, 12.17 cm-2; and m-plane, 6.44 cm-2). Specifically, at room temperature and under about 40% humidity with a scan speed of 0.5 μm/s, the height of oxides on a- and m-planes 4H-SiC is 6.5 and 13 nm, respectively, whereas the height of oxides on the c-plane increased up to 30 nm. In addition, the results of AFM-LO with thermally grown oxides on the different plane orientations in SiC are compared.

No MeSH data available.