Highly Efficient Near-IR Photoluminescence of Er Immobilized in Mesoporous SBA-15.

Xue YL, Wu P, Liu Y, Zhang X, Lin L, Jiang Q - Nanoscale Res Lett (2010)

Bottom Line: It is a 29.3% boost in fluorescent cross section compared to what has been obtained in conventional silica.The upconversion coefficient in Yb-Er-SBA-15 is relatively small compared to that in other ordinary glass hosts.The increased fluorescent cross section and lowered upconversion coefficient could benefit for the high-gain optical amplifier.

View Article: PubMed Central - HTML - PubMed

ABSTRACT
SiO(2) mesoporous molecular sieve SBA-15 with the incorporation of erbium ions is studied as a novel type of nanoscopic composite photoluminescent material in this paper. To enhance the photoluminescence efficiency, two schemes have been used for the incorporation of Er(3+) where (1) Er(3+) is ligated with bis-(perfluoromethylsulfonyl)-aminate (PMS) forming Er(PMS)(x)-SBA-15 and (2) Yb(3+) is codoped with Er(3+) forming Yb-Er-SBA-15. As high as 11.17 × 10(-21)cm(2) of fluorescent cross section at 1534 nm and 88 nm of "effective bandwidth" have been gained. It is a 29.3% boost in fluorescent cross section compared to what has been obtained in conventional silica. The upconversion coefficient in Yb-Er-SBA-15 is relatively small compared to that in other ordinary glass hosts. The increased fluorescent cross section and lowered upconversion coefficient could benefit for the high-gain optical amplifier. Finally, the Judd-Ofelt theory has also been used for the analyses of the optical spectra of Er(PMS)(x)-SBA-15.

No MeSH data available.


EDS energy spectrum of Er(PMS)x-SBA-1
© Copyright Policy
Related In: Results  -  Collection


getmorefigures.php?uid=PMC2991226&req=5

Figure 5: EDS energy spectrum of Er(PMS)x-SBA-1

Mentions: The EDS energy spectrum of Er(PMS)x-SBA-15 in Fig. 5 clearly displays the energy distribution of Er3+. That almost same diagrams obtained from the measurement at different parts of the sample demonstrates a uniform inclusion of Er3+ complexes in the pores of SBA-15.


Highly Efficient Near-IR Photoluminescence of Er Immobilized in Mesoporous SBA-15.

Xue YL, Wu P, Liu Y, Zhang X, Lin L, Jiang Q - Nanoscale Res Lett (2010)

EDS energy spectrum of Er(PMS)x-SBA-1
© Copyright Policy
Related In: Results  -  Collection

Show All Figures
getmorefigures.php?uid=PMC2991226&req=5

Figure 5: EDS energy spectrum of Er(PMS)x-SBA-1
Mentions: The EDS energy spectrum of Er(PMS)x-SBA-15 in Fig. 5 clearly displays the energy distribution of Er3+. That almost same diagrams obtained from the measurement at different parts of the sample demonstrates a uniform inclusion of Er3+ complexes in the pores of SBA-15.

Bottom Line: It is a 29.3% boost in fluorescent cross section compared to what has been obtained in conventional silica.The upconversion coefficient in Yb-Er-SBA-15 is relatively small compared to that in other ordinary glass hosts.The increased fluorescent cross section and lowered upconversion coefficient could benefit for the high-gain optical amplifier.

View Article: PubMed Central - HTML - PubMed

ABSTRACT
SiO(2) mesoporous molecular sieve SBA-15 with the incorporation of erbium ions is studied as a novel type of nanoscopic composite photoluminescent material in this paper. To enhance the photoluminescence efficiency, two schemes have been used for the incorporation of Er(3+) where (1) Er(3+) is ligated with bis-(perfluoromethylsulfonyl)-aminate (PMS) forming Er(PMS)(x)-SBA-15 and (2) Yb(3+) is codoped with Er(3+) forming Yb-Er-SBA-15. As high as 11.17 × 10(-21)cm(2) of fluorescent cross section at 1534 nm and 88 nm of "effective bandwidth" have been gained. It is a 29.3% boost in fluorescent cross section compared to what has been obtained in conventional silica. The upconversion coefficient in Yb-Er-SBA-15 is relatively small compared to that in other ordinary glass hosts. The increased fluorescent cross section and lowered upconversion coefficient could benefit for the high-gain optical amplifier. Finally, the Judd-Ofelt theory has also been used for the analyses of the optical spectra of Er(PMS)(x)-SBA-15.

No MeSH data available.