Biosorption of Lanthanides from Aqueous Solutions Using Pretreated Buccinum tenuissimum Shell Biomass.

Koto Y, Kano N, Wang Y, Sakamoto N, Imaizumi H - Bioinorg Chem Appl (2010)

Bottom Line: Biosorption experiment from aqueous solutions containing known amount of rare earth elements (REEs) using pre-treated Buccinum tenuissimum shell was explored to evaluate the efficiency of shell biomass as sorbent for REEs.In this work, four kinds of sieved shell samples: (a) "Ground original sample", (b) "Heat-treatment (480°C, 6 hours) sample", (c) "Heat-treatment (950°C, 6 hours) sample" and (d) "Heat-treatment (950°C, 6 hours) and water added sample" were used.Furthermore, to confirm the characteristics of the shell biomass, the crystal structure, the surface morphology, and the specific surface area of these shell samples were determined.

View Article: PubMed Central - PubMed

Affiliation: Graduate School of Science and Technology, Niigata University, Ikarashi 2-nocho 8050, Nishi-Ku, Niigata 950-2181, Japan.

ABSTRACT
Biosorption experiment from aqueous solutions containing known amount of rare earth elements (REEs) using pre-treated Buccinum tenuissimum shell was explored to evaluate the efficiency of shell biomass as sorbent for REEs. In this work, four kinds of sieved shell samples: (a) "Ground original sample", (b) "Heat-treatment (480°C, 6 hours) sample", (c) "Heat-treatment (950°C, 6 hours) sample" and (d) "Heat-treatment (950°C, 6 hours) and water added sample" were used. Furthermore, to confirm the characteristics of the shell biomass, the crystal structure, the surface morphology, and the specific surface area of these shell samples were determined. Consequently, the following matters have been mainly clarified. (1) The crystal structure of the shell biomass was transformed from aragonite (CaCO(3)) into calcite (CaCO(3)) phase by heat-treatment (480°C, 6 hours); then mainly transformed into calcium oxide (CaO) by heat-treatment (950°C, 6 hours), and calcium hydroxide (Ca(OH)(2)) by heat-treatment (950°C, 6 hours) and adding water. (2) The shell biomass showed excellent sorption capacity for lanthanides. (3) Adsorption isotherms using the shell biomass can be described by Langmuir and Freundlich isotherms satisfactorily for lanthanides except "heat-treatment (950°C, 6 hours) sample". (4) Shell biomass (usually treated as waste material) can be an efficient sorbent for lanthanides in future.

No MeSH data available.


Related in: MedlinePlus

X-ray diffraction (XRD) patterns of Buccinum tenussimum shell biomass before adsorption of metals. (a) ground original sample, (b) heat-treatment (480°C) sample, (c) heat-treatment (950°C) sample, and (d) heat-treatment (950°C) and water-added sample.
© Copyright Policy - open-access
Related In: Results  -  Collection


getmorefigures.php?uid=PMC2963800&req=5

fig1: X-ray diffraction (XRD) patterns of Buccinum tenussimum shell biomass before adsorption of metals. (a) ground original sample, (b) heat-treatment (480°C) sample, (c) heat-treatment (950°C) sample, and (d) heat-treatment (950°C) and water-added sample.

Mentions: X-ray powder diffraction (XRD) patterns of the four kinds of Buccinum tenuissimum shell biomass samples are shown in Figure 1. The crystal structure of the shell biomass was transformed from aragonite (CaCO3) into calcite (CaCO3) phase by heat treatment (480°C, 6 hours). Moreover, the crystal structure of the shell biomass was mainly transformed into calcium oxide (CaO) by heat treatment (950°C, 6 hours) and was mainly transformed into calcium hydroxide (Ca(OH)2) by adding water after heat treatment (950°C, 6 hours).


Biosorption of Lanthanides from Aqueous Solutions Using Pretreated Buccinum tenuissimum Shell Biomass.

Koto Y, Kano N, Wang Y, Sakamoto N, Imaizumi H - Bioinorg Chem Appl (2010)

X-ray diffraction (XRD) patterns of Buccinum tenussimum shell biomass before adsorption of metals. (a) ground original sample, (b) heat-treatment (480°C) sample, (c) heat-treatment (950°C) sample, and (d) heat-treatment (950°C) and water-added sample.
© Copyright Policy - open-access
Related In: Results  -  Collection

Show All Figures
getmorefigures.php?uid=PMC2963800&req=5

fig1: X-ray diffraction (XRD) patterns of Buccinum tenussimum shell biomass before adsorption of metals. (a) ground original sample, (b) heat-treatment (480°C) sample, (c) heat-treatment (950°C) sample, and (d) heat-treatment (950°C) and water-added sample.
Mentions: X-ray powder diffraction (XRD) patterns of the four kinds of Buccinum tenuissimum shell biomass samples are shown in Figure 1. The crystal structure of the shell biomass was transformed from aragonite (CaCO3) into calcite (CaCO3) phase by heat treatment (480°C, 6 hours). Moreover, the crystal structure of the shell biomass was mainly transformed into calcium oxide (CaO) by heat treatment (950°C, 6 hours) and was mainly transformed into calcium hydroxide (Ca(OH)2) by adding water after heat treatment (950°C, 6 hours).

Bottom Line: Biosorption experiment from aqueous solutions containing known amount of rare earth elements (REEs) using pre-treated Buccinum tenuissimum shell was explored to evaluate the efficiency of shell biomass as sorbent for REEs.In this work, four kinds of sieved shell samples: (a) "Ground original sample", (b) "Heat-treatment (480°C, 6 hours) sample", (c) "Heat-treatment (950°C, 6 hours) sample" and (d) "Heat-treatment (950°C, 6 hours) and water added sample" were used.Furthermore, to confirm the characteristics of the shell biomass, the crystal structure, the surface morphology, and the specific surface area of these shell samples were determined.

View Article: PubMed Central - PubMed

Affiliation: Graduate School of Science and Technology, Niigata University, Ikarashi 2-nocho 8050, Nishi-Ku, Niigata 950-2181, Japan.

ABSTRACT
Biosorption experiment from aqueous solutions containing known amount of rare earth elements (REEs) using pre-treated Buccinum tenuissimum shell was explored to evaluate the efficiency of shell biomass as sorbent for REEs. In this work, four kinds of sieved shell samples: (a) "Ground original sample", (b) "Heat-treatment (480°C, 6 hours) sample", (c) "Heat-treatment (950°C, 6 hours) sample" and (d) "Heat-treatment (950°C, 6 hours) and water added sample" were used. Furthermore, to confirm the characteristics of the shell biomass, the crystal structure, the surface morphology, and the specific surface area of these shell samples were determined. Consequently, the following matters have been mainly clarified. (1) The crystal structure of the shell biomass was transformed from aragonite (CaCO(3)) into calcite (CaCO(3)) phase by heat-treatment (480°C, 6 hours); then mainly transformed into calcium oxide (CaO) by heat-treatment (950°C, 6 hours), and calcium hydroxide (Ca(OH)(2)) by heat-treatment (950°C, 6 hours) and adding water. (2) The shell biomass showed excellent sorption capacity for lanthanides. (3) Adsorption isotherms using the shell biomass can be described by Langmuir and Freundlich isotherms satisfactorily for lanthanides except "heat-treatment (950°C, 6 hours) sample". (4) Shell biomass (usually treated as waste material) can be an efficient sorbent for lanthanides in future.

No MeSH data available.


Related in: MedlinePlus